Marble
Throughout the centuries we find in the whole world grand palaces, temples and structures built out of marble. It is a stone that resists the wear of time and adds greatness wherever it is applied.
GGM-Preben presents you with a collection of the best marbles from Spain, Italy (Carrera), Turkey, Bulgaria and having at the top of the list the Royal White marble of Kozani, originating from Greece, a country world-known for it’s elegant monuments.
GGM-Preben presents you with a collection of the best marbles from Spain, Italy (Carrera), Turkey, Bulgaria and having at the top of the list the Royal White marble of Kozani, originating from Greece, a country world-known for it’s elegant monuments.
ROYAL WHITE KOZANIS
| TEST | RESULTS |
|---|---|
| Absoption coefficient | 0.08 wt% |
| Compressive strength | 97.00 MPa |
| Modulus of rapture | 12.90 MPa |
| Abrasion resistance | 2.65 mm |
| Calcite | 98 % |
| Dolomite | 1 % |
| Quartz | 1 % |
SEMI WHITE KOZANIS
| TEST | RESULTS |
|---|---|
| Absoption coefficient | 0.08 wt% |
| Compressive strength | 97.00 MPa |
| Modulus of rapture | 12.90 MPa |
| Abrasion resistance | 2.65 mm |
| Calcite | 98 % |
| Dolomite | 1 % |
| Quartz | 1 % |
FOUME KOZANIS
| TEST | RESULTS |
|---|---|
| Absorption Coefficient | 0.08 wt% |
| Compressive Strength | 97.00 MPa |
| Modulus Of Rupture | 12.90 MPa |
| Abrasion resistance | 2.65 mm |
| Calcite | 98 % |
| Dolomite | 1 % |
| Quartz | 1 % |
RODITIS
| TEST | RESULTS |
|---|---|
| Absoption coefficient | 0.07 wt% |
| Compressive strength | 63.00 MPa |
| Modulus of rapture | 20.00 MPa |
| Abrasion resistance | 2.28 mm |
| Calcite | 97 % |
| Dolomite | 2 % |
| Quartz | 1 % |
BRESCIA SINAI
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
33.9 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1600 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
20200 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.26 % |
| Density [ ASTM C97 ] |
2662 Kg / m3 |
GALALA
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
33.9 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1600 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
20200 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.26 % |
| Density [ ASTM C97 ] |
2662 Kg / m3 |
KHATEMYA
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
35.7 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1800 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
21300 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.87 % |
| Density [ ASTM C97 ] |
2590 Kg / m3 |
SAMAHA
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
35.7 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1800 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
21300 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.87 % |
| Density [ ASTM C97 ] |
2590 Kg / m3 |
SILVIA DARK
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
26.7 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1000 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
1400 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
10400 Psi |
| Absorbation by Weight [ ASTM C97 ] |
1.62 % |
| Density [ ASTM C97 ] |
2478 Kg / m3 |
SILVIA LIGHT
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
26.7 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1000 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
1500 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
10400 Psi |
| Absorbation by Weight [ ASTM C97 ] |
1.62 % |
| Density [ ASTM C97 ] |
2478 Kg / m3 |
SUNNY DARK
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
26.4 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1600 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
13300 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.30 % |
| Density [ ASTM C97 ] |
– |
SUNNY LIGHT
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
26.4 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1600 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
2000 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
13300 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.30 % |
| Density [ ASTM C97 ] |
2618 Kg / m3 |
TERIESTA
| TEST (ACCORDING TO ASTM STANDARDS) | RESULTS |
|---|---|
| Abrasion resistance Hardness [ ASTM C241 / C1353 ] |
38.8 Ha |
| Flexural Strength Mpa [ ASTM C880 ] |
1900 Psi |
| Modulus Of Rupture Mpa. [ ASTM C99 ] |
1900 Psi |
| Compressive Strength Mpa. [ ASTM C170 ] |
19800 Psi |
| Absorbation by Weight [ ASTM C97 ] |
0.89 % |
| Density [ ASTM C97 ] |
2628 Kg / m3 |
SIVEC WHITE
| TEST | RESULTS |
|---|---|
| Abrasion resistance (after 1000 m) | 6.58 mm |
| Modulus Of Rupture | 132 Kg / cm2 |
| Compression Strength | 990 Kg / cm2 |
| Absorption Coefficient | 0.23 wt% |
| Apparent Specific Weight | 2770 Kg / m3 |
| Microhardness Knoop | 321.6 Kg / mm2 |
| Calcite | 8 % |
| Dolomite | 90 % |
| Quartz | 2 % |
THASSOS WHITE
| TEST | RESULTS |
|---|---|
| Abrasion resistance (after 1000 m) | 6.58 mm |
| Modulus Of Rupture | 132 Kg / cm2 |
| Compression Strength | 990 Kg / cm2 |
| Absorption Coefficient | 0.23 wt% |
| Apparent Specific Weight | 2850 Kg / m3 |
| Microhardness Knoop | 321.6 Kg / mm2 |
| Calcite | 12 % |
| Dolomite (%) | 86 % |
| Quartz | 2 % |
VRATZA
| TEST | RESULTS |
|---|---|
| Reaction to fire | Class A1 |
| Flexural strength | 18.8 MPa |
| Resistance to fixings | 1850 N |
| Water absorption at atmospheric pressure | 5.1 % per mass |
| Water absorption coefficient by capillarity | 15.53 g / (m2 x sec0,5) |
| Apparent density | 2250 kg / m3 |
| Open porosity | 16.4 % per volume |
| Abrasion resistance | 19683 mm3 (loss in volume) |
CREMA MARFIL
| TEST | RESULTS |
|---|---|
| Compression Strenght | 122,84 MPa |
| Bending Strenght | 19,41 MPa |
| Volumetric Weight | 2,72 gm / cm3 |
| Friction Wear Resistance | 0,35 mm |
| Porosity | 0,10 % |
| Knoop Micro-hardness | 1774,5 MPa |
| Absorption Coefficient | 0,15 % |
| Impact Test (minimum height) | 42 cms |
DARK EMPERADOR
| TEST | RESULTS |
|---|---|
| Compression Strenght | 136,47 MPa |
| Bending Strenght | 25,98 MPa |
| Volumetric Weight | 2,65 gm / cm3 |
| Friction Wear Resistance | 0,4 mm |
| Porosity | 1,20 % |
| Knoop Micro-hardness | 1839,21 MPa |
| Absorption Coefficient | 0,40 % |
| Impact Test (minimum height) | 46 cms |
DIONYSSOS
| TEST | RESULTS |
|---|---|
| Reaction to fire | Class A1 |
| Flexural strength | 18.9 MPa |
| Resistance to fixings | 1950 N |
| Compressive strength | 91 MPa |
| Water absorption at atmospheric pressure | 0.1 % per mass |
| Water absorption coefficient by capillarity | 0.173 g / (m2 x sec0,5) |
| Apparent density | 2720 kg / m3 |
| Open porosity | 0.3 % per volume |
| Abrasion resistance | 21378 mm3 (loss in volume) |
LIGHT EMPERADOR
| TEST | RESULTS |
|---|---|
| Hardness | 3,5-4 Mohs |
| Unit Volume Weight | 2650 Kg / m3 |
| Density | 2680 Kg / m3 |
| Porosity | 0,1 % |
| Water Absorbation | 0,35 % |
| Compressive Strenght | 958 Kg / cm2 |
CARRARA
| TEST | RESULTS |
|---|---|
| Absorbtion by weight (C97) |
0.11 % |
| Density (C97) |
169.73 lbs/ft3 |
| Compressive strenght (C170) |
12,972 psi |
| Abrasion resist. Hardness (C241) |
15.04 |
| Flexural strength (C880) |
697 psi |
KOKY BEIGE
SANDWAVE
ADONIS PEARL
ADONIS ROSE
CAPPUCINO
LIMESTONE